{"id":1368,"date":"2024-10-25T08:34:58","date_gmt":"2024-10-25T08:34:58","guid":{"rendered":"https:\/\/nbaem.com\/?p=1368"},"modified":"2024-10-25T08:36:15","modified_gmt":"2024-10-25T08:36:15","slug":"how-to-make-ndfeb-magnet","status":"publish","type":"post","link":"https:\/\/nbaem.com\/hu\/how-to-make-ndfeb-magnet\/","title":{"rendered":"Hogyan k\u00e9sz\u00edts\u00fcnk NdFeB m\u00e1gneset"},"content":{"rendered":"
\n
\n
\n

Neod\u00edmium m\u00e1gnes<\/a> <\/span>m\u00e9g mindig a leger\u0151sebb \u00e9s leggyakrabban haszn\u00e1lt ritkaf\u00f6ldf\u00e9mes \u00e1lland\u00f3 m\u00e1gneses anyag napjainkban. A neod\u00edmium m\u00e1gnes a gy\u00e1rt\u00e1si folyamat szerint szinterelt neod\u00edmium m\u00e1gnesre, k\u00f6t\u00f6tt neod\u00edmium m\u00e1gnesre \u00e9s forr\u00f3 pr\u00e9selt neod\u00edmium m\u00e1gnesre oszthat\u00f3. Minden forma m\u00e1s m\u00e1gneses tulajdons\u00e1gokkal rendelkezik, \u00edgy alkalmaz\u00e1si ter\u00fclet\u00fck r\u00e9szben \u00e1tfed\u0151 \u00e9s kieg\u00e9sz\u00edt\u0151 kapcsolatban \u00e1ll egym\u00e1ssal. A m\u00e1gnesfelhaszn\u00e1l\u00f3k k\u00edv\u00e1ncsiak arra, hogyan k\u00e9sz\u00fclnek a neod\u00edmium m\u00e1gnesek. A szinterelt neod\u00edmium m\u00e1gnes hagyom\u00e1nyos porf\u00e9mes elj\u00e1r\u00e1ssal k\u00e9sz\u00fcl, \u00e9s abszol\u00fat dominanci\u00e1t \u00e9lvez a piaci r\u00e9szesed\u00e9sben.<\/span><\/p>\n<\/div>\n<\/div>\n

\n
\n
\n

Hogyan k\u00e9sz\u00fclnek a neod\u00edmium m\u00e1gnesek?<\/strong><\/p>\n

Szinterelt neod\u00edmium m\u00e1gnes k\u00e9sz\u00fcl az alapanyagok v\u00e1kuumban vagy inert atmoszf\u00e9r\u00e1ban t\u00f6rt\u00e9n\u0151 olvaszt\u00e1s\u00e1val indukci\u00f3s olvaszt\u00f3ban, majd a szalagk\u00e9sz\u00edt\u0151ben feldolgozva \u00e9s leh\u0171tve Nd-Fe-B \u00f6tv\u00f6zet szalagot k\u00e9pezve. Az \u00f6tv\u00f6zet szalagokat finom porr\u00e1 \u0151rlik, amelynek \u00e1tm\u00e9r\u0151je n\u00e9h\u00e1ny mikron. A finom port ezut\u00e1n ir\u00e1ny\u00edtott m\u00e1gneses t\u00e9rben t\u00f6m\u00f6r\u00edtik, majd szinterezik s\u0171r\u0171 testekk\u00e9. A testeket ezut\u00e1n a k\u00edv\u00e1nt form\u00e1kra megmunk\u00e1lj\u00e1k, fel\u00fcletkezelik \u00e9s m\u00e1gnesess\u00e9 teszik.<\/p>\n

S\u00falyoz\u00e1s<\/strong><\/p>\n

Az alkalmas nyersanyag s\u00falyoz\u00e1sa k\u00f6zvetlen\u00fcl \u00f6sszef\u00fcgg a m\u00e1gnes \u00f6sszet\u00e9tel\u00e9nek pontoss\u00e1g\u00e1val. A nyersanyag tisztas\u00e1ga vagy a k\u00e9miai \u00f6sszet\u00e9tel stabilit\u00e1sa a term\u00e9kmin\u0151s\u00e9g alapja. A szinterelt neod\u00edmium m\u00e1gnes \u00e1ltal\u00e1ban ritkaf\u00f6ldf\u00e9m \u00f6tv\u00f6zetet v\u00e1laszt, mint p\u00e9ld\u00e1ul Praseod\u00edmium-Neod\u00edmium mischmetal, Lant\u00e1n-C\u00e9zium mischmetal, \u00e9s Dysprosium Vas Dy-Fe \u00f6tv\u00f6zetet k\u00f6lts\u00e9g okokb\u00f3l. Magas olvad\u00e1spont\u00fa elemk\u00e9nt B\u00f3r, Molibd\u00e9n vagy Ni\u00f3bium ker\u00fcl hozz\u00e1ad\u00e1sra ferro\u00f6tv\u00f6zet form\u00e1j\u00e1ban. A rozsda r\u00e9teg, a szennyez\u0151d\u00e9s, az oxid \u00e9s a szennyez\u0151d\u00e9s a nyersanyag fel\u00fclet\u00e9n mikrohomokf\u00fav\u00f3 g\u00e9ppel sz\u00fcks\u00e9ges elt\u00e1vol\u00edtani. Emellett a nyersanyagnak megfelel\u0151 m\u00e9ret\u0171nek kell lennie, hogy megfeleljen a k\u00e9s\u0151bbi olvaszt\u00e1si folyamat hat\u00e9konys\u00e1g\u00e1nak. A neod\u00edmium alacsony p\u00e1rolg\u00e1si nyom\u00e1ssal \u00e9s akt\u00edv k\u00e9miai tulajdons\u00e1gokkal rendelkezik, ez\u00e9rt a ritkaf\u00f6ldf\u00e9mek egy bizonyos m\u00e9rt\u00e9k\u0171 volatiliz\u00e1ci\u00f3s vesztes\u00e9get \u00e9s oxid\u00e1ci\u00f3s vesztes\u00e9get szenvednek az olvaszt\u00e1si folyamat sor\u00e1n, ez\u00e9rt a szinterelt neod\u00edmium m\u00e1gnes s\u00falyoz\u00e1si folyamat\u00e1ban figyelembe kell venni tov\u00e1bbi ritkaf\u00f6ldf\u00e9m hozz\u00e1ad\u00e1s\u00e1t a m\u00e1gnes \u00f6sszet\u00e9tel\u00e9nek pontoss\u00e1g\u00e1nak biztos\u00edt\u00e1sa \u00e9rdek\u00e9ben.<\/p>\n<\/div>\n<\/div>\n<\/div>\n<\/div>\n

\n
\n
\n
\n

Olvaszt\u00e1s \u00e9s szalag\u00f6nt\u00e9s<\/strong><\/p>\n<\/div>\n<\/div>\n

\n
\n

Olvaszt\u00e1s \u00e9s szalag\u00f6nt\u00e9s alapvet\u0151 a \u00f6sszet\u00e9tel, krist\u00e1ly\u00e1llapot \u00e9s f\u00e1ziseloszl\u00e1s szempontj\u00e1b\u00f3l, \u00edgy befoly\u00e1solja a k\u00e9s\u0151bbi folyamatokat \u00e9s a m\u00e1gneses teljes\u00edtm\u00e9nyt. A nyersanyagot k\u00f6zepes \u00e9s alacsony frekvenci\u00e1j\u00fa indukci\u00f3s olvaszt\u00e1ssal hev\u00edtik, v\u00e1kuum vagy inert atmoszf\u00e9r\u00e1ban. Az \u00f6nt\u00e9s akkor v\u00e9gezhet\u0151 el, amikor az \u00f6tv\u00f6zet olvad\u00e9k homogeniz\u00e1l\u00f3dott, ki\u00fcr\u00fclt \u00e9s szennyez\u0151d\u00e9sekt\u0151l megtisztult. Egy j\u00f3 \u00f6nt\u00f6tt \u00f6ntv\u00e9ny mikrostrukt\u00far\u00e1j\u00e1nak j\u00f3l n\u00f6v\u0151 \u00e9s finom m\u00e9ret\u0171 oszlopos krist\u00e1lyokat kell tartalmaznia, majd az Nd- gazdag f\u00e1zisnak a szemcseszeg\u00e9ly ment\u00e9n kell eloszlani. Emellett az \u00f6nt\u00f6tt \u00f6ntv\u00e9ny mikrostrukt\u00far\u00e1j\u00e1nak mentesnek kell lennie \u03b1-Fe f\u00e1zist\u00f3l. A Re-Fe f\u00e1zis diagramja azt mutatja, hogy a ritkaf\u00f6ldf\u00e9m-tri\u00e1ris \u00f6tv\u00f6zet elker\u00fclhetetlen\u00fcl \u03b1-Fe f\u00e1zist eredm\u00e9nyez lass\u00fa h\u0171t\u00e9s sor\u00e1n. Az \u03b1-Fe f\u00e1zis szobah\u0151m\u00e9rs\u00e9kleti l\u00e1gy m\u00e1gneses tulajdons\u00e1gai s\u00falyosan rontj\u00e1k a m\u00e1gnes teljes\u00edtm\u00e9ny\u00e9t, ez\u00e9rt gyors h\u0171t\u00e9ssel kell g\u00e1tolni a keletkez\u00e9s\u00e9t. Annak \u00e9rdek\u00e9ben, hogy a k\u00edv\u00e1nt gyors h\u0171t\u00e9si hat\u00e1s el\u00e9r\u00e9s\u00e9vel g\u00e1toljuk az \u03b1-Fe f\u00e1zis k\u00e9pz\u0151d\u00e9s\u00e9t, a Showa Denko K. K. kifejlesztette a Szalag\u00f6nt\u00e9si Technol\u00f3gi\u00e1t, amely hamarosan az ipar rutintechnol\u00f3gi\u00e1j\u00e1v\u00e1 v\u00e1lt. Az Nd- gazdag f\u00e1zis egyenletes eloszl\u00e1sa \u00e9s az \u03b1-Fe f\u00e1zisra gyakorolt g\u00e1tl\u00f3 hat\u00e1s hat\u00e9konyan cs\u00f6kkenti a ritkaf\u00f6ldf\u00e9mek \u00f6ssztartalm\u00e1t, ez kedvez\u0151 a magas teljes\u00edtm\u00e9ny\u0171 m\u00e1gnes gy\u00e1rt\u00e1s\u00e1ban \u00e9s a k\u00f6lts\u00e9gek cs\u00f6kkent\u00e9s\u00e9ben.<\/p>\n

Hidrog\u00e9n dekrepit\u00e1ci\u00f3<\/strong><\/p>\n<\/div>\n<\/div>\n

\n
\n

A ritka f\u00f6ldf\u00e9mek, \u00f6tv\u00f6zetek vagy intermet\u00e1lkompoundok hidrog\u00e9nez\u00e9si viselked\u00e9se \u00e9s a hidrid fizikai-k\u00e9miai tulajdons\u00e1gai mindig fontos k\u00e9rd\u00e9s volt a ritka f\u00f6ldek alkalmaz\u00e1s\u00e1ban. A Nd-Fe-B \u00f6tv\u00f6zet\u00f6ntv\u00e9ny is nagyon er\u0151s hidrog\u00e9nez\u00e9si hajlamot mutat. A hidrog\u00e9natomok az intermet\u00e1lkompound f\u0151 f\u00e1zis \u00e9s a Nd-ban gazdag szemcsesz\u00e9l k\u00f6z\u00f6tti interstici\u00e1lis helyre l\u00e9pnek be, \u00e9s interstici\u00e1lis vegy\u00fcletet k\u00e9peznek. Ezut\u00e1n megn\u0151 az atomk\u00f6zi t\u00e1vols\u00e1g \u00e9s b\u0151v\u00fcl a r\u00e1cst\u00e9rfogat. A keletkez\u0151 bels\u0151 fesz\u00fclts\u00e9g reped\u00e9seket okoz a szemcsesz\u00e9lben (intergranul\u00e1ris t\u00f6r\u00e9s), krist\u00e1lyt\u00f6r\u00e9st (transzkrisztall\u00e1ris t\u00f6r\u00e9s) vagy ductilis t\u00f6r\u00e9st. Ezek a reped\u00e9sek ropog\u00e1ssal j\u00e1rnak, ez\u00e9rt hidrog\u00e9n reped\u00e9snek (hidrog\u00e9n decrepitation) nevezik \u0151ket. A szinterelt neod\u00edmium m\u00e1gnes hidrog\u00e9n reped\u00e9s\u00e9nek folyamata is HD folyamatk\u00e9nt ismert. A hidrog\u00e9n reped\u00e9s sor\u00e1n keletkez\u0151 szemcsesz\u00e9l reped\u00e9sek \u00e9s krist\u00e1lyt\u00f6r\u00e9sek kialakul\u00e1sa Az NdFeB tanfolyam por rendk\u00edv\u00fcl t\u00f6r\u00e9keny \u00e9s rendk\u00edv\u00fcl el\u0151ny\u00f6s a k\u00e9s\u0151bbi sz\u00f3r\u00f3malmi folyamat szempontj\u00e1b\u00f3l. A sz\u00f3r\u00f3malmi folyamat hat\u00e9konys\u00e1g\u00e1nak n\u00f6vel\u00e9se mellett a hidrog\u00e9n reped\u00e9sk\u00e9pz\u0151d\u00e9ses folyamat is kedvez\u0151 az finom por \u00e1tlagos szemcsem\u00e9ret\u00e9nek be\u00e1ll\u00edt\u00e1s\u00e1hoz.<\/span><\/p>\n<\/div>\n<\/div>\n<\/div>\n<\/div>\n

\n
\n
\n
\n

Jet \u0151rl\u00e9s<\/strong><\/p>\n

A jet milling a porfeldolgoz\u00e1s legpraktikusabb \u00e9s leghat\u00e9konyabb megold\u00e1s\u00e1nak bizonyult. A jet milling inert g\u00e1z magas sebess\u00e9g\u0171 sug\u00e1rz\u00e1s\u00e1t haszn\u00e1lja arra, hogy a durva port szuperszonikus sebess\u00e9gre gyors\u00edtsa, \u00e9s a port egym\u00e1snak csap\u00f3djon. A porfeldolgoz\u00e1s alapvet\u0151 c\u00e9lja a megfelel\u0151 \u00e1tlagos r\u00e9szecskem\u00e9ret \u00e9s r\u00e9szecskem\u00e9ret-eloszl\u00e1s keres\u00e9se. A fent eml\u00edtett jellemz\u0151k k\u00fcl\u00f6nb\u00f6z\u0151 makroszk\u00f3pos tulajdons\u00e1gokat mutatnak, amelyek k\u00f6zvetlen\u00fcl befoly\u00e1solj\u00e1k a por t\u00f6lt\u00e9s\u00e9t, orient\u00e1ci\u00f3j\u00e1t, t\u00f6m\u00f6r\u00edt\u00e9s\u00e9t, form\u00e1z\u00e1s\u00e1t \u00e9s a szinterel\u00e9s sor\u00e1n keletkez\u0151 mikrostrukt\u00far\u00e1t, ez\u00e1ltal \u00e9rz\u00e9kenyen hatva a m\u00e1gneses teljes\u00edtm\u00e9nyre, mechanikai tulajdons\u00e1gokra, termoelectricit\u00e1sra \u00e9s a szinterelt Neod\u00edmium m\u00e1gnes k\u00e9miai stabilit\u00e1s\u00e1ra. Az ide\u00e1lis mikrostrukt\u00fara finom \u00e9s egys\u00e9ges f\u0151 f\u00e1zis szemcs\u00e9je, amelyet sima \u00e9s v\u00e9kony m\u00e1sodlagos f\u00e1zis vesz k\u00f6r\u00fcl. Emellett a f\u0151 f\u00e1zis szemcs\u00e9j\u00e9nek k\u00f6nny\u0171 m\u00e1gnesezhet\u0151s\u00e9gi ir\u00e1ny\u00e1t a lehet\u0151 legink\u00e1bb \u00f6sszhangban kell elhelyezni az orient\u00e1ci\u00f3s ir\u00e1nnyal. A h\u00e9zagok, nagy szemcs\u00e9k vagy l\u00e1gy m\u00e1gneses f\u00e1zis jelent\u0151sen cs\u00f6kkentik a bels\u0151 coercivit\u00e1st. A remanencia \u00e9s a sz\u00f6gletess\u00e9g a demagnetiz\u00e1ci\u00f3s g\u00f6rb\u00e9n egyidej\u0171leg cs\u00f6kken, mik\u00f6zben a szemcs\u00e9k k\u00f6nny\u0171 m\u00e1gnesezhet\u0151s\u00e9gi ir\u00e1nya elt\u00e9r az orient\u00e1ci\u00f3s ir\u00e1nyt\u00f3l. Ez\u00e9rt az \u00f6tv\u00f6zeteket szil\u00e1rd krist\u00e1lyszemcs\u00e9kre kell apr\u00edtani, amelyek \u00e1tm\u00e9r\u0151je 3-5 mikron k\u00f6z\u00f6tt van.<\/p>\n

S\u0171r\u00edt\u00e9s<\/strong><\/p>\n<\/div>\n<\/div>\n

\n
\n

A m\u00e1gneses t\u00e9r orient\u00e1ci\u00f3s t\u00f6m\u00f6r\u00edt\u00e9st arra haszn\u00e1lj\u00e1k, hogy a m\u00e1gneses por \u00e9s a k\u00fcls\u0151 m\u00e1gneses t\u00e9r k\u00f6z\u00f6tti k\u00f6lcs\u00f6nhat\u00e1st kihaszn\u00e1lva a port az egyszer\u0171 m\u00e1gnesez\u00e9si ir\u00e1ny ment\u00e9n igaz\u00edts\u00e1k, \u00e9s ez \u00f6sszhangban legyen a v\u00e9gs\u0151 m\u00e1gnesez\u00e9si ir\u00e1nnyal. A m\u00e1gneses t\u00e9r orient\u00e1ci\u00f3s t\u00f6m\u00f6r\u00edt\u00e9s a leggyakoribb m\u00f3dszer az anizotr\u00f3p m\u00e1gnes gy\u00e1rt\u00e1s\u00e1ra. A Nd-Fe-B \u00f6tv\u00f6zetet kor\u00e1bban jet \u0151rl\u00e9si folyamat sor\u00e1n egyszemcs\u00e9s krist\u00e1lyr\u00e9szecsk\u00e9kre t\u00f6rt\u00e9k. Az egyszemcs\u00e9s krist\u00e1lyr\u00e9szecske uniaxi\u00e1lis anizotr\u00f3pi\u00e1val rendelkezik, \u00e9s mindegyiknek csak egy egyszer\u0171 m\u00e1gnesez\u00e9si ir\u00e1nya van. A m\u00e1gneses por k\u00fcls\u0151 hat\u00e1s\u00e1ra egy t\u00f6bbdom\u00e9nes \u00e1llapotb\u00f3l egydom\u00e9nes \u00e1llapotba alakul. A m\u00e1gneses t\u00e9r a form\u00e1ba laz\u00e1n bet\u00f6lt\u00e9s ut\u00e1n, majd az egyszer\u0171 m\u00e1gnesez\u00e9si ir\u00e1ny c-tengely\u00e9nek be\u00e1ll\u00edt\u00e1sa az k\u00fcls\u0151 m\u00e1gneses t\u00e9r ir\u00e1ny\u00e1val val\u00f3 \u00f6sszhang \u00e9rdek\u00e9ben forgat\u00e1ssal vagy mozgat\u00e1ssal. Az \u00f6tv\u00f6zetpor c-tengely\u00e9nek elrendez\u00e9se alapvet\u0151en megmaradt a t\u00f6m\u00f6r\u00edt\u00e9si folyamat sor\u00e1n. A t\u00f6m\u00f6r\u00edtett r\u00e9szeket demagnetiz\u00e1ci\u00f3s kezel\u00e9ssel kell ell\u00e1tni a form\u00e1z\u00e1s el\u0151tt. A t\u00f6m\u00f6r\u00edt\u00e9si folyamat legfontosabb mutat\u00f3ja az orient\u00e1ci\u00f3 m\u00e9rt\u00e9ke. A szinterelt neod\u00edmium m\u00e1gnesek orient\u00e1ci\u00f3s fok\u00e1t k\u00fcl\u00f6nb\u00f6z\u0151 t\u00e9nyez\u0151k befoly\u00e1solj\u00e1k, bele\u00e9rtve az orient\u00e1ci\u00f3s m\u00e1gneses t\u00e9r er\u0151ss\u00e9g\u00e9t, r\u00e9szecskem\u00e9retet, l\u00e1tsz\u00f3lagos s\u0171r\u0171s\u00e9get, t\u00f6m\u00f6r\u00edt\u00e9si m\u00f3dszert, t\u00f6m\u00f6r\u00edt\u00e9si nyom\u00e1st stb.<\/span><\/p>\n<\/div>\n<\/div>\n<\/div>\n<\/div>\n

\n
\n
\n
\n

Szintr\u00e9s<\/strong><\/p>\n<\/div>\n<\/div>\n

\n
\n

A t\u00f6m\u00f6r\u00edtett alkatr\u00e9sz s\u0171r\u0171s\u00e9ge a feldolgozott szinterez\u00e9si folyamat ut\u00e1n el\u00e9rheti a t\u00f6bb mint 95% elm\u00e9leti s\u0171r\u0171s\u00e9get magas v\u00e1kuumban vagy tiszta inert atmoszf\u00e9r\u00e1ban. Ez\u00e9rt a szinterelt neod\u00edmium m\u00e1gnesben l\u00e9v\u0151 \u00fcregek z\u00e1rtak, ami biztos\u00edtja a m\u00e1gneses fluxus s\u0171r\u0171s\u00e9g\u00e9nek egyenletess\u00e9g\u00e9t \u00e9s k\u00e9miai stabilit\u00e1s\u00e1t. Mivel a szinterelt neod\u00edmium m\u00e1gnesek \u00e1lland\u00f3 m\u00e1gneses tulajdons\u00e1gai szorosan kapcsol\u00f3dnak saj\u00e1t mikrostrukt\u00far\u00e1jukhoz, a szinterez\u00e9s ut\u00e1ni h\u0151kezel\u00e9s szint\u00e9n kritikus a m\u00e1gneses teljes\u00edtm\u00e9ny, k\u00fcl\u00f6n\u00f6sen a bels\u0151 coercit\u00e1s be\u00e1ll\u00edt\u00e1s\u00e1ban. Az Nd- gazdag szemhat\u00e1rf\u00e1zis folyad\u00e9kf\u00e1zisk\u00e9nt szolg\u00e1l, amely k\u00e9pes el\u0151seg\u00edteni a szinterez\u00e9si reakci\u00f3t \u00e9s helyre\u00e1ll\u00edtani a fel\u00fcleti hib\u00e1kat a f\u0151 f\u00e1zis szem\u00e9ben. A neod\u00edmium m\u00e1gnes szinterez\u00e9si h\u0151m\u00e9rs\u00e9klete \u00e1ltal\u00e1ban 1050 \u00e9s 1180 Celsius-fok k\u00f6z\u00f6tt mozog. A t\u00fal magas h\u0151m\u00e9rs\u00e9klet szemn\u00f6veked\u00e9shez vezet \u00e9s cs\u00f6kkenti a bels\u0151 coercit\u00e1st. Az ide\u00e1lis bels\u0151 coercit\u00e1s, a demagnetiz\u00e1ci\u00f3s g\u00f6rbe n\u00e9gyzetess\u00e9ge \u00e9s a magas h\u0151m\u00e9rs\u00e9kleten irreverzibilis vesztes\u00e9g el\u00e9r\u00e9s\u00e9hez a szinterelt neod\u00edmium m\u00e1gnes \u00e1ltal\u00e1ban k\u00e9tl\u00e9pcs\u0151s temper\u00e1l\u00e1si h\u0151kezel\u00e9st ig\u00e9nyel 900 \u00e9s 500 Celsius-fokon.<\/p>\n

G\u00e9pi megmunk\u00e1l\u00e1s<\/strong><\/p>\n

A szabv\u00e1nyos m\u00e9ret\u0171, k\u00f6zepes m\u00e9ret\u0171 szinterelt Neod\u00edmium m\u00e1gnes mellett a m\u00e1gneses mez\u0151 ir\u00e1ny\u00edt\u00e1s\u00e1nak \u00f6sszet\u00f6m\u00f6r\u00edt\u00e9si folyamat\u00e1ban fenn\u00e1ll\u00f3 technikai korl\u00e1tok miatt neh\u00e9z az els\u0151 pr\u00f3b\u00e1lkoz\u00e1sra a k\u00edv\u00e1nt alakot \u00e9s m\u00e9retpontoss\u00e1got el\u00e9rni, ez\u00e9rt a megmunk\u00e1l\u00e1s elker\u00fclhetetlen folyamat a szinterelt Neod\u00edmium m\u00e1gnes eset\u00e9ben. Mint tipikus cermet anyag, a szinterelt Neod\u00edmium m\u00e1gnes meglehet\u0151sen kem\u00e9ny \u00e9s t\u00f6r\u00e9keny, \u00edgy csak v\u00e1g\u00e1s, f\u00far\u00e1s \u00e9s csiszol\u00e1s lehets\u00e9ges. alkalmazhat\u00f3 a hagyom\u00e1nyos megmunk\u00e1l\u00e1si technol\u00f3gi\u00e1k k\u00f6z\u00f6tt a megmunk\u00e1l\u00e1si folyamat\u00e1ban. A penge v\u00e1g\u00e1s \u00e1ltal\u00e1ban gy\u00e9m\u00e1ntbevonat\u00fa vagy CBN-bevonat\u00fa peng\u00e9t haszn\u00e1l. A huzalszab\u00e1s \u00e9s l\u00e9zeres v\u00e1g\u00e1s j\u00f3l alkalmas speci\u00e1lis alak\u00fa m\u00e1gnes megmunk\u00e1l\u00e1s\u00e1ra, de egyidej\u0171leg alacsony gy\u00e1rt\u00e1si hat\u00e9konys\u00e1ggal \u00e9s magas feldolgoz\u00e1si k\u00f6lts\u00e9gekkel v\u00e1dolj\u00e1k. A szinterelt Neod\u00edmium m\u00e1gnes f\u00far\u00e1si folyamata els\u0151sorban gy\u00e9m\u00e1ntot \u00e9s l\u00e9zert alkalmaz. Sz\u00fcks\u00e9ges a trepanning folyamat kiv\u00e1laszt\u00e1sa, amikor a gy\u0171r\u0171 m\u00e1gnes bels\u0151 lyuka nagyobb, mint 4 mm. A trepanning folyamat mell\u00e9kterm\u00e9kek\u00e9nt keletkez\u0151 trepanned magot m\u00e1s, kisebb m\u00e1gnesek gy\u00e1rt\u00e1s\u00e1ra lehet felhaszn\u00e1lni, ez\u00e1ltal jelent\u0151sen n\u00f6velve az anyag kihaszn\u00e1lts\u00e1gi ar\u00e1ny\u00e1t. A m\u00e1sol\u00e1si k\u00f6sz\u00f6r\u0171k\u0151 a k\u00f6sz\u00f6r\u00fcl\u0151 fel\u00fclet alapj\u00e1n k\u00e9sz\u00fcl.<\/span><\/p>\n<\/div>\n<\/div>\n<\/div>\n<\/div>\n

\n
\n
\n

Fel\u00fcletkezel\u00e9s<\/strong><\/p>\n<\/div>\n<\/div>\n

\n
\n

Fel\u00fcleti v\u00e9d\u0151kezel\u00e9s sz\u00fcks\u00e9ges elj\u00e1r\u00e1s a Neod\u00edmium m\u00e1gnes eset\u00e9ben, k\u00fcl\u00f6n\u00f6sen a sintered Neod\u00edmium m\u00e1gnesn\u00e9l. A sintered Neod\u00edmium m\u00e1gnes t\u00f6bbf\u00e1zis\u00fa mikrostrukt\u00far\u00e1val rendelkezik, \u00e9s mag\u00e1ban foglalja az Nd2Fe14B f\u0151f\u00e1zist, az Nd- gazdag f\u00e1zist \u00e9s a B-gazdag f\u00e1zist. Az Nd-gazdag f\u00e1zis rendk\u00edv\u00fcl er\u0151s oxid\u00e1ci\u00f3s hajlamot mutat, \u00e9s a nedves k\u00f6rnyezetben els\u0151dleges akkumul\u00e1tork\u00e9nt fog viselkedni a f\u0151f\u00e1zissal. Kis mennyis\u00e9g\u0171 helyettes\u00edt\u0151 elemek k\u00e9pesek n\u00f6velni a m\u00e1gnesek k\u00e9miai stabilit\u00e1s\u00e1t, de ez a m\u00e1gneses teljes\u00edtm\u00e9ny rov\u00e1s\u00e1ra megy. Ez\u00e9rt a sintered Neod\u00edmium m\u00e1gnes v\u00e9delme els\u0151sorban a fel\u00fclet\u00e9re ir\u00e1nyul. A sintered Neod\u00edmium m\u00e1gnes fel\u00fcleti kezel\u00e9se lehet nedves \u00e9s sz\u00e1raz folyamat. Nedves folyamat alatt \u00e9rtj\u00fck, amikor a m\u00e1gneseket tiszta v\u00edzben vagy oldatban v\u00e9gzik a fel\u00fcleti v\u00e9d\u0151kezel\u00e9st. A nedves folyamat mag\u00e1ban foglalja a foszf\u00e1tos, galvaniz\u00e1l\u00e1st, galvaniz\u00e1l\u00e1s n\u00e9lk\u00fcli bevonatol\u00e1st, elektrof\u00f3rezist, sz\u00f3r\u00f3bevonatot \u00e9s mer\u00edt\u00e9ses bevonatot. A sz\u00e1raz folyamat fizikai vagy k\u00e9miai folyamat r\u00e9v\u00e9n t\u00f6rt\u00e9n\u0151 fel\u00fcleti v\u00e9d\u0151kezel\u00e9st jelent oldattal val\u00f3 \u00e9rintkez\u00e9s n\u00e9lk\u00fcl. A sz\u00e1raz folyamat \u00e1ltal\u00e1ban fizikai p\u00e1rologtat\u00e1sos (PVD) \u00e9s k\u00e9miai p\u00e1rologtat\u00e1sos (CVD) m\u00f3dszereket foglal mag\u00e1ban.<\/p>\n

M\u00e1gneses polariz\u00e1ci\u00f3<\/strong><\/p>\n<\/div>\n<\/div>\n

\n
\n

A legt\u00f6bb \u00e1lland\u00f3 m\u00e1gnest a rendeltet\u00e9sszer\u0171 alkalmaz\u00e1suk el\u0151tt m\u00e1gnesezik. A m\u00e1gnesez\u00e9si folyamat mag\u00e1ban foglalja m\u00e1gneses mez\u0151 alkalmaz\u00e1s\u00e1t az \u00e1lland\u00f3 m\u00e1gnes orient\u00e1ci\u00f3s ir\u00e1ny\u00e1ban, \u00e9s a megn\u00f6vekedett k\u00fcls\u0151 m\u00e1gneses t\u00e9r er\u0151ss\u00e9g\u00e9vel el\u00e9ri a technikai tel\u00edtetts\u00e9get. Minden t\u00edpus\u00fa \u00e1lland\u00f3 m\u00e1gneses anyagnak k\u00fcl\u00f6nb\u00f6z\u0151 m\u00e1gneses t\u00e9r er\u0151ss\u00e9gre van sz\u00fcks\u00e9ge ahhoz, hogy a m\u00e1gnesez\u00e9si ir\u00e1nyban el\u00e9rje a technikai tel\u00edtetts\u00e9get. A remanencia \u00e9s a bels\u0151 koercitivit\u00e1s alacsonyabb lesz a megfelel\u0151 \u00e9rt\u00e9kein\u00e9l, ha a k\u00fcls\u0151 m\u00e1gneses t\u00e9r er\u0151ss\u00e9ge alacsonyabb, mint a technikai tel\u00edtetts\u00e9g m\u00e1gneses tere. Az \u00e1lland\u00f3 m\u00e1gnes izotr\u00f3p \u00e9s anizotr\u00f3p t\u00edpusra oszthat\u00f3 aszerint, hogy van-e k\u00f6nny\u0171 m\u00e1gnesez\u00e9si ir\u00e1nya vagy nincs. Nagy bels\u0151 koercitivit\u00e1s\u00fa anizotr\u00f3p m\u00e1gnesk\u00e9nt a szinterezett neod\u00edmium m\u00e1gnest impulzus m\u00e1gnesez\u00e9ssel kell m\u00e1gnesezni. A kondenz\u00e1tor a helyesb\u00edt\u00e9s ut\u00e1n felt\u00f6lt\u0151dik, majd a kondenz\u00e1torban l\u00e9v\u0151 elektromos energia pillanatszer\u0171en kis\u00fcl a m\u00e1gnesez\u0151 k\u00e9sz\u00fcl\u00e9kbe. A m\u00e1gnesez\u0151 k\u00e9sz\u00fcl\u00e9k pulz\u00e1l\u00f3 m\u00e1gneses teret gener\u00e1lhat a rajta \u00e1tfoly\u00f3 pillanatnyi er\u0151s \u00e1ram sor\u00e1n. Ez\u00e9rt a tekercsben l\u00e9v\u0151 \u00e1lland\u00f3 m\u00e1gnes m\u00e1gnesezve lesz. A szinterezett neod\u00edmium m\u00e1gnesen k\u00fcl\u00f6nf\u00e9le m\u00e1gnesez\u00e9si mint\u00e1k \u00e9rhet\u0151k el, amennyiben azok nem \u00fctk\u00f6znek az orient\u00e1ci\u00f3s ir\u00e1ny\u00e1val.<\/span><\/p>\n<\/div>\n<\/div>\n<\/div>","protected":false},"excerpt":{"rendered":"

Neod\u00edmium m\u00e1gnes m\u00e9g mindig a leger\u0151sebb \u00e9s leggyakrabban haszn\u00e1lt ritkaf\u00f6ldf\u00e9m \u00e1lland\u00f3 m\u00e1gneses anyag ma. A neod\u00edmium m\u00e1gnes oszthat\u00f3 szinterelt neod\u00edmium m\u00e1gnesre, k\u00f6t\u00f6tt neod\u00edmium m\u00e1gnesre \u00e9s forr\u00f3 pr\u00e9selt neod\u00edmium m\u00e1gnesre a gy\u00e1rt\u00e1si folyamat szerint. Minden forma m\u00e1s-m\u00e1s m\u00e1gneses tulajdons\u00e1gokkal rendelkezik, majd azok \u00e1tfed\u00e9se [\u2026]<\/p>","protected":false},"author":1,"featured_media":0,"comment_status":"open","ping_status":"open","sticky":false,"template":"","format":"standard","meta":{"om_disable_all_campaigns":false,"_mi_skip_tracking":false,"footnotes":""},"categories":[1],"tags":[],"class_list":["post-1368","post","type-post","status-publish","format-standard","hentry","category-uncategorized"],"jetpack_featured_media_url":"","_links":{"self":[{"href":"https:\/\/nbaem.com\/hu\/wp-json\/wp\/v2\/posts\/1368","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/nbaem.com\/hu\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/nbaem.com\/hu\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/nbaem.com\/hu\/wp-json\/wp\/v2\/users\/1"}],"replies":[{"embeddable":true,"href":"https:\/\/nbaem.com\/hu\/wp-json\/wp\/v2\/comments?post=1368"}],"version-history":[{"count":3,"href":"https:\/\/nbaem.com\/hu\/wp-json\/wp\/v2\/posts\/1368\/revisions"}],"predecessor-version":[{"id":1371,"href":"https:\/\/nbaem.com\/hu\/wp-json\/wp\/v2\/posts\/1368\/revisions\/1371"}],"wp:attachment":[{"href":"https:\/\/nbaem.com\/hu\/wp-json\/wp\/v2\/media?parent=1368"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/nbaem.com\/hu\/wp-json\/wp\/v2\/categories?post=1368"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/nbaem.com\/hu\/wp-json\/wp\/v2\/tags?post=1368"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}